Portland Grey Cement Turkey ports FOB Prices

Portland Grey Cement Turkey ports FOB Prices

Quantity:
Up to 10,000 / 50.000  Mt per Month


Terms of delivery :
FOB     port of any /  safe in a Mediterranean, Marmara sea,black sea Ports,Turkey    (Seller Option).


Price:
1)Cement CEM I 42,5 R .................. 50 USD / MT. FOB From Turkey ports 50Kg bags
2)Cement CEM I 42,5 R .................. 52 USD / MT. FOB From Turkey ports 25Kg bags


3)Cement CEM II 42,5 R ................. 48 USD / MT. FOB From Turkey ports 50Kg bags
4)Cement CEM II 42,5 R ................. 50 USD / MT. FOB From Turkey ports 25Kg bags


Loading port :
Turkey ports


daily loading rate :
2.000 - 4.000 between

Payment :
According to proforma invoice %30 of advance payment for commencement of production by factory for each shipment or agreed quantity.  Remain  balance  % 70 should be paid   10 days before loading of the vessel.


Delivery :
Delivery will be after 10 days completion of the payment and will be subject to mutual aggreement.

Lay-Can :
To be advised from cement factory regarding to port availability & production Schedule of the factory.


Inspection :
Seller’s account at where house the time of loading by SGS or  equivalent.  (Seller Option).






MUSA YAPI / Cement & Clinker Trading

WEB : www.musayapi.com.tr
E-MAIL : musayapi@musayapi.com.tr
musayapi@gmail.com

Cement 42,5 R N Portland   / Republic of Turkey / Mediterrenean

Zement 42,5 / Republik Türkei, / Mittelmeer.

цемент 42,5. / Турецкая Республика , / Средиземноморья.

cemento 42.5 / Turcia, / Marea Mediterană.

cimenter 42,5. / République de Turquie , / de la Méditerranée

cimentar 42,5. / Repubblica di Turchia, / Mediterranean.

42,5 cemento. / República de Turquía,/ Mediterráneo.

τσιμέντο 42,5. / Δημοκρατίας της Τουρκίας ,/ της Μεσογείου .

ცემენტის 42,5 თურქეთის რესპუბლიკაში, / ხმელთაშუა.

أسمنت 42،5. جمهورية تركيا. / البحر الأبيض المتوسط.

מלט 42,5. / רפובליקה של טורקיה. / ים תיכוני.

#Clinker - RAW NATURAL GYPSUM

Clinker FOB Prices Turkey

loading: Turkey ports FOB

- Grey Portland Clinker  FOB USD 28.00  Mtons

- Sulphate Resistant Clinker  FOB usd 39 Mtons

#GreyPortlandClinker  

#SulphateResistantClinker  

#Cement #Clinker #Bauxite ore #Basalt Stone #Limestone

Portland Cement Clinker (Gray)

Hydraulic binder that is used as main constituent of cements described under EN 197-1:2011

- Clinker that is suitable for production of Portland Cements

- Clinker that is suitable for production of Sulfate Resistance Cements

Low Alkali Portland Cement Clinker (Gray)

Hydraulic binder that is used as main constituent of cements described under ASTM C150, ASTM C595 and ASTM C1157.

- Suitable for production of low alkali cements.

- Suitable for production of Cement type ASTM C150 TYPE I/II

- Suitable for production of Cement type ASTM C150 TYPE V

web: www.musayapi.com.tr
E-mail: export@musayapi.com.tr
musayapi@gmail.com

GYPSUM STONE

GYPSUM 

GYPSUM ROCK

NATURAL GYPSUM ROCK

TURKISH GYPSUM STONE

PURE GYPSUM STONE

BULK SHIP GYPSUM STONE

GYPSUM ORE FOR THE CEMENT INDUSTRY 

GYPSUM STONE FOR THE CEMENT INDUSTRY 

EXPORT GYPSUM & GYPSUM STONE

GYPSUM STONE PRICE

GYPSUM STONE FOB

#Portland #Grey #Cement #Turkey #ports #FOB #Prices

Portland Grey Cement Turkey ports FOB Prices

Quantity:
Up to 10,000 / 50.000  Mt per Month


Terms of delivery :
FOB     port of any /  safe in a Mediterranean, Marmara sea,black sea Ports,Turkey    (Seller Option).


Price:
1)Cement CEM I 42,5 R .................. 50 USD / MT. FOB From Turkey ports 50Kg bags
2)Cement CEM I 42,5 R .................. 52 USD / MT. FOB From Turkey ports 25Kg bags


3)Cement CEM II 42,5 R ................. 48 USD / MT. FOB From Turkey ports 50Kg bags
4)Cement CEM II 42,5 R ................. 50 USD / MT. FOB From Turkey ports 25Kg bags


Loading port :
Turkey ports


daily loading rate :
2.000 - 4.000 between

Payment :
According to proforma invoice %30 of advance payment for commencement of production by factory for each shipment or agreed quantity.  Remain  balance  % 70 should be paid   10 days before loading of the vessel.


Delivery :
Delivery will be after 10 days completion of the payment and will be subject to mutual aggreement.

Lay-Can :
To be advised from cement factory regarding to port availability & production Schedule of the factory.


Inspection :
Seller’s account at where house the time of loading by SGS or  equivalent.  (Seller Option).





MUSA YAPI / Cement & Clinker Trading

WEB : www.musayapi.com.tr
E-MAIL : musayapi@musayapi.com.tr
musayapi@gmail.com

Composite cement (CEM V/A (S-P-V) 32.5 R)

Composite cement

Portland Composite Cement is produced by milling clinker, limestone and some hydraulic material and a given amount of gypsum. They are classified into two according to the amount of additives in them. Type A includes 6-20% limestone by weight and type B includes 21-35% slug by weight. Portland Composite Cement is classified into six types according to their early strength periods within 28 days: PKC 32.5, PKC 32.5R, PKC 42.5, PKC 42.5R, PKC 52.5, PKC 52.5R. This cement type is newly adopted from European standards. 

A hydraulic cement obtained by milling 40-64 parts (by weight) of Portland cement clinker together with a corresponding amount (60-36 parts) of suitable additives and a certain quantity of gypsum. 

It conforms to the TS EN 197-1 

Used in all concrete structures, road pavements, foundations and retaining walls, water arcs, dams, wall adhesives and mortars, concrete pipes, in industrial work grounds contaminated with medium level sulfate, refineries and in general-purpose construction works where a low hydration temperature is needed. 

Composite cement (CEM V/A (S-P-V) 32.5 R)

A hydraulic cement obtained by milling 40-64 parts (by weight) of Portland cement clinker together with a corresponding amount (60-36 parts) of suitable additives and a certain quantity of gypsum. 

It conforms to the TS EN 197-1 

Used in all concrete structures, road pavements, foundations and retaining walls, water arcs, dams, wall adhesives and mortars, concrete pipes, in industrial work grounds contaminated with medium level sulfate, refineries and in general-purpose construction works where a low hydration temperature is needed. Filds of use include:

• General purpose
• All kinds of concrete structures
• Road pavements
• Foundation and retaining walls
• Water arcs
• Dams
• Plaster and wall mortar
• Concrete pipes
• Industrial site grounds with medium level sulfate
• Refineries

PORTLAND COMPOSITE CEMENT  CEM II 42.5  N    B-M (P-L) 

Chemical analysis	Results (%)	Limit values
Silicon Oxide, % SiO2	23,34
Aluminium Oxide, % Al2O3	6,61
Iron Oxide, % Fe2O3	3,16
Calcium Oxide, % CaO	55,86
Magnesium Oxide, % MgO	1,41
Sulphur Oxide, % SO3	2,55	≤ 3,5%
Sodium Oxide, % Na2O	0,80
Potassium Oxide, % K2O	1,25
CI	0,0160	≤ 0,10%
Loss on Ignition % ( L.O.I)	7,86
Free lime	0,87
Total Additive	26,84	21-35

Physical analysis	Results	Limit values
Initial Setting Time (minutes)	180	≥ 60
Final Setting Time (minutes)	275
Soundness/Expansion (mm)	1,0	≤ 10
Specific Surface Area Blaine (cm2/g)	4321
2 days - Compressive Strength (MPa)	18,0	≥ 10
7 days - Compressive Strength (MPa)	30,7
28 days - Compressive Strength (MPa)	45,9	≥ 42,5; ≤ 62,5

The best raw materials and Minerals, ores – we procure high-quality raw materials for you from Turkey in the quantities and types you require.

PORTLAND COMPOSITE CEMENT    CEM II  32.5 R     B-M (P-L)

Chemical analysis	Results (%)	Limit values
Silicon Oxide, % SiO2	24,84
Aluminium Oxide, % Al2O3	7,51
Iron Oxide, % Fe2O3	3,18
Calcium Oxide, % CaO	51,49
Magnesium Oxide, % MgO	1,55
Sulphur Oxide, % SO3	2,43	≤ 4,0%
Sodium Oxide, % Na2O	1,15
Potassium Oxide, % K2O	1,56
CI	0,0164	≤ 0,10%
Loss on Ignition % ( L.O.I)	6,63
Free lime	0,83
Total Additive	32,87	21-35%

Physical analysis	Results	Limit values
Initial Setting Time (minutes)	175	≥ 75
Final Setting Time (minutes)	265
Soundness/Expansion (mm)	1,0	≤ 10
Specific Surface Area Blaine (cm2/g)	3851
2 days - Compressive Strength (MPa)	15,7	≥ 20
7 days - Compressive Strength (MPa)	28,9
28 days - Compressive Strength (MPa)	38,6	≥ 32,5; ≤ 52,5

PORTLAND COMPOSITE CEMENT CEM II 42.5 R A-M (P-L)

PORTLAND COMPOSITE CEMENT     CEM II  42.5 R    A-M (P-L)

Chemical analysis	Results (%)	Limit values
Silicon Oxide, % SiO2	23,14
Aluminium Oxide, % Al2O3	6,48
Iron Oxide, % Fe2O3	3,17
Calcium Oxide, % CaO	57,14
Magnesium Oxide, % MgO	1,47
Sulphur Oxide, % SO3	2,59	Max. 4,0%
Sodium Oxide, % Na2O	0,66
Potassium Oxide, % K2O	1,13
CI	0,0046	Max. 0,10%
Loss on Ignition % ( L.O.I)	6,13
Free lime	0,97
Total Additive	18,42	12-20%

Physical analysis	Results	Limit values
Initial Setting Time (minutes)	170	Min. 60
Final Setting Time (minutes)	265
Soundness/Expansion (mm)	1,0	Max. 10
Specific Surface Area Blaine (cm2/g)	4251
2 days - Compressive Strength (MPa)	23,0	Min. 20
7 days - Compressive Strength (MPa)	35,8
28 days - Compressive Strength (MPa)	50,1	42,5 – 62,5